| SiC | ≥98% |
| SiO2 | ≤1% |
| H2O3 | ≤0.5% |
| Fe2O3 | ≤0.3% |
| F.C | ≤0.3% |
| 磁性物含量 | ≤0.02% |
| 莫氏硬度: | 9.2 |
| 努普硬度 | 3000-3300 kg/mm2 |
| 维氏硬度 | 2940-3200 kg/mm2 |
| 熔点 | 2300 °C游离 |
| Max使用温度 | 1900℃ |
| 比重: | 3.2-3.45 g/cm3 |
| 堆积密度(LPD): | 1.2-1.6 g/cm3(根据粒度有所不同) |
| 颜色: | 黑色 |
| 晶体形状: | 六方晶系 |
| 弹性模量 | 58-65x106 psi |
| 热膨胀系数 | 3.9-4.5 x10-6/ ℃ |
| 热导率 | 71-130 W/MK |
| JIS粒度 | D0(微米) | D3(微米) | D50(微米) | D94(微米) |
| #240 | ≤ 127 | ≤ 103 | 57.0±3.0 | ≥ 40 |
| #280 | ≤ 112 | ≤ 87 | 48.0±3.0 | ≥ 33 |
| #320 | ≤ 98 | ≤ 74 | 40.0±2.5 | ≥ 27 |
| #360 | ≤ 86 | ≤ 66 | 35.0±2.0 | ≥ 23 |
| #400 | ≤ 75 | ≤ 58 | 30.0±2.0 | ≥ 20 |
| #500 | ≤ 63 | ≤ 50 | 25.0±2.0 | ≥ 16 |
| #600 | ≤ 53 | ≤ 41 | 20.0±1.5 | ≥ 13 |
| #700 | ≤ 45 | ≤ 37 | 17.0±1.5 | ≥ 11 |
| #800 | ≤ 38 | ≤ 31 | 14.0±1.0 | ≥ 9.0 |
| #1000 | ≤ 32 | ≤ 27 | 11.5.±1.0 | ≥ 7.0 |
| #1200 | ≤ 27 | ≤ 23 | 9.5±0.8 | ≥ 5.5 |
| #1500 | ≤ 23 | ≤ 20 | 8.0±0.6 | ≥ 4.5 |
| #2000 | ≤ 19 | ≤ 17 | 6.7±0.6 | ≥ 4.0 |
| #2500 | ≤ 16 | ≤ 14 | 5.5±0.5 | ≥ 3.0 |
| #3000 | ≤ 13 | ≤ 11 | 4.0±0.5 | ≥ 2.0 |
| #4000 | ≤ 11 | ≤ 8.0 | 3.0±0.4 | ≥ 1.8 |
| 粒度 | 最粗粒 | 粗粒 | 基本粒 | 混合粒 | 细粒 | |||||
| 尺寸范围(um) | 允许颗粒 | 尺寸范围(um) | 重量%不多于 | 尺寸范围(um) | 重量%不少于 | 尺寸范围(um) | 重量%不少于 | 尺寸范围(um) | 重量%不多于 | |
| W63 | 100-80 | 1 | 80-63 | 15 | 63-50 | 50 | 63-40 | 80 | 细于40 | 5 |
| W50 | 80-63 | 1 | 63-50 | 15 | 50-40 | 50 | 50-28 | 80 | 细于28 | 5 |
| W40 | 63-50 | 1 | 50-40 | 15 | 40-28 | 50 | 40-20 | 80 | 细于20 | 5 |
| W28 | 50-40 | 1 | 40-28 | 18 | 28-20 | 45 | 28-14 | 74 | 细于14 | 8 |
| W20 | 40-28 | 1 | 28-20 | 18 | 20-14 | 45 | 20-10 | 74 | 细于10 | 8 |
| W14 | 28-20 | 2 | 20-14 | 20 | 10-14 | 45 | 14-7 | 72 | 细于7 | 8 |
| W10 | 20-14 | 2 | 10-14 | 20 | 10-7 | 40 | 10-5 | 70 | 细于5 | 10 |
| W7 | 10-14 | 2 | 10-7 | 20 | 7-5 | 40 | 7-3.5 | 70 | 细于3.5 | 10 |
| W5 | 10-7 | 3 | 7-5 | 20 | 5-3.5 | 40 | 5-2.5 | 70 | 细于2.5 | 10 |
| P标微粉 | D0（um） | D3(um) | D50(um) | D95(um) |
| P240 | Max. 110 | Max. 81.7 | 58.5±2.0 | Min. 44.5 |
| P280 | Max. 101 | Max. 74.0 | 52.2±2.0 | Min. 39.2 |
| P320 | Max. 94 | Max. 66.8 | 46.2±1.5 | Min. 34.2 |
| P360 | Max. 87 | Max. 60.3 | 40.5±1.5 | Min. 29.6 |
| P400 | Max. 81 | Max. 53.9 | 35.0±1.5 | Min. 25.2 |
| P500 | Max. 77 | Max. 48.3 | 30.2±1.5 | Min. 21.5 |
| P600 | Max. 72 | Max. 43.0 | 25.8±1.0 | Min. 18.0 |
| P800 | Max. 67 | Max. 38.1 | 21.8±1.0 | Min. 15.1 |
| P1000 | Max. 63 | Max. 33.7 | 18.3±1.0 | Min. 12.4 |
| P1200 | Max. 58 | Max. 29.7 | 15.3±1.0 | Min. 10.2 |
| P1500 | Max. 53 | Max. 22.4 | 12.6±1.0 | Min. 8.3 |
| P2000 | Max. 45 | Max. 19.3 | 10.3±0.8 | Min. 6.7 |
| P2500 | Max. 38 | Max. 14.0 | 8.4±0.5 | Min. 5.4 |
| P3000 | Max. 32 | Max. 12.0 | 6.7±0.5 | Min. 3.0 |
| P4000 | Max. 27 | Max. 11.0 | 5.5±0.5 | Min. 2.0 |
| P5000 | Max. 23 | Max. 8.0 | 4±0.5 | Min. 1.8 |