Hardness: HV/维氏硬度 | 3280-3400kg/mm2 |
Hardness: Mohs/莫氏硬度 | 9.4-9.5 |
Specific Gravity/比重 | 3.2 g/cm3 |
Particle Shape/颗粒形态 | Fine powder/细小粉末 |
Color/颜色 | Green/绿色 |
Bulk density(LPD)/堆积密度 | 0.76-0.80 g/cm3 |
Crystal shape/晶型 | Hexagonal/六方晶型 |
Melting Point/熔点 | dissociated at about 2600°C/2600°C游离 |
Maximum service temperature/使用温度上限 | 1900°C |
Thermal conductivity/导热系数 | 0.013 cal/cm2.sec (900°C) |
Thermal expansion coefficient/热膨胀系数 | 7-9 x10-6 /°C (0-1600°C) |
Chemical Item/化学成分 | Guarantee Value/保证值(%) | Typical Value/典型值(%) |
SiC/碳化硅 | ≥98.5% | 98.76 |
Free Si/游离硅 | ≤0.2 | 0.13 |
Free C/游离碳 | ≤0.3 | 0.20 |
Fe2O3/三氧化二铁 | ≤0.15 | 0.11 |
SiO2/二氧化硅 | ≤0.3 | 0.24 |
Size粒径 | Guarantee Value/保证值 | Typical Value/典型值 |
D10(um) | ≥2 | 3.031 |
D50(um) | 4.4-5.4 | 5.288 |
D90(um) | ≤9 | 8.807 |